江苏q345钢管的焊接工艺@q345钢材的屈服强度值
纵向力学性能
|
标准 |
牌号 |
抗拉强度
(MPa) |
屈服强度(MPa) ≥ |
延伸率(%)
≥ |
|
≤16 |
>16mm |
|
GB/T8163-1999 |
10 |
335-475 |
205 |
195 |
24 |
|
20 |
410-550 |
245 |
235 |
20 |
|
Q295 |
430-610 |
295 |
285 |
22 |
|
Q345 |
490-665 |
325 |
315 |
21 |
化学成份
|
标准 |
牌号 |
C |
Si |
Mn |
P≤ |
S≤ |
Ni≤ |
Cu≤ |
Cr≤ |
|
GB/T8163-1999 |
10 |
0.07-0.14 |
0.17-0.37 |
0.35-0.65 |
0.035 |
0.035 |
0.25 |
0.15 |
0.25 |
|
20 |
0.17-0.24 |
0.17-0.37 |
0.35-0.65 |
0.035 |
0.035 |
0.25 |
0.25 |
0.25 |
|
Q295 A |
≤0.16 |
≤0.55 |
0.80-1.50 |
0.045 |
0.045 |
0.30 |
0.30 |
0.30 |
|
Q295 B |
≤0.16 |
≤0.55 |
0.80-1.50 |
0.040 |
0.040 |
0.30 |
0.30 |
0.30 |
|
Q345 A |
≤0.20 |
≤0.55 |
1.00-1.60 |
0.045 |
0.045 |
0.30 |
0.30 |
0.30 |
|
Q345 B |
≤0.20 |
≤0.55 |
1.00-1.60 |
0.040 |
0.040 |
0.30 |
0.30 |
0.30 |
|
Q345 C |
≤0.20 |
≤0.55 |
1.00-1.60 |
0.035 |
0.035 |
0.30 |
0.30 |
0.30 |
|
Q345 D |
≤0.18 |
≤0.55 |
1.00-1.60 |
0.030 |
0.030 |
0.30 |
0.30 |
0.30 |
|
Q345 E |
≤0.18 |
≤0.55 |
1.00-1.60 |
0.025 |
0.025 |
0.30 |
0.30 |
0.30 |
Q345低合金管属低合金系列----低合金高强度结构钢(GB/T1591-1994)。
Q345A、B、C、D、E是此类钢的代表牌号，其中Q345A合金管、Q345B合金管级钢通常称16Mn，此种材质为最普通；
Q345低合金管表示方法：Q代表的是这种材质的屈服，后面的345，就是指这种材质的屈服值，在345左右。(类同于Q235的命名方法)并会随着材质的厚度的增加而使其屈服值减小。
低合金高强度结构钢除含有一定量硅或锰基本元素外，还含有其他适合我国资源情况的元素。如钒(V)、铌(Nb)、钛(Ti)、铝(Al)、钼(Mo)、氮(N)、和稀土(RE)等微量元素。按化学成分和性能要求，其牌号由Q295A、B，Q345A、B、C、D、E，Q390A、B、C、D、E，Q420A、B、C、D、E，Q460C、D、E等钢级表示，其含义同碳素结构钢。
Q345低合金管同碳素结构钢比。具有强度高、综合性能好、使用寿命长、应用范围广、比较经济等优点。该钢多轧制成板材、型材、无缝钢管等，被广泛用于桥梁、船舶、锅炉、车辆及重要建筑结构中。
Q345A，Q345B，Q345C，Q345D，Q345E。这是等级的区分，所代表的，主要是冲击的温度有所不同。
Q345A级，是不做冲击;Q345B级，是20度常温冲击;Q345C级，是0度冲击;Q345D级，是－20度冲击;Q345E级，是－40度冲击。在不同的冲击温度，冲击的数值也有所不同。
|